Reactivity-Informed Machine Learning for Performance Prediction and Design Space Exploration of Alkali-Activated Slag

Establishing quantitative relationships among mix design, raw material properties, curing conditions, and performance remains a long-standing challenge in cementitious materials, particularly for alkali-activated materials with variable precursor and activator chemistry. Here, we curated the largest literature-derived alkali-activated slag (AAS) dataset to date, comprising over 3100 compressive strength records, 155 chemically distinct ground granulated blast-furnace slags (GGBSs), and 24 attributes incorporating precursor chemistry, fineness, and reactivity. Multiple machine learning (ML) algorithms were benchmarked across progressively enriched feature scenarios, demonstrating that integrating GGBS compositions, fineness, curing conditions, and specimen geometry improves predictive performance. The average metal oxide dissociation energy (AMODE), a physically interpretable representation of precursor reactivity, provides a compact alternative descriptor to explicit oxide compositions while enabling comparable predictive performance. Model interpretation revealed physically consistent trends from heterogeneous data, including non-monotonic effects of Na2O dosage and silicate modulus, reduced predicted strength at higher water content and larger specimen size, and coupled oxide-level effects more coherently represented by AMODE than by individual oxide contents. Statistically constrained design space exploration reveals reactivity-dependent trade-offs among strength, embodied CO2 emissions, and cost. The design maps identify high-strength regions with substantially lower CO2 emissions than OPC-based references at similar cost. Overall, this work demonstrates how reactivity-informed ML can extract physically meaningful trends from heterogeneous AAS data and guide source-dependent binder design. The curated dataset is publicly accessible to support advances in cement and concrete research.